CF-1801(1802)

Product Description

100% E-fiberglass texturized yarn,1/3 Twill structure

Dipped by PTFE emulsion (laminated with dedicated ePTFE membranes)

Fluffy yarn substrate, with good covering ability, good air permeability, achieved surface-filtration by hot-pressing dedicated ePTFE membranes on body, and with high filtration efficiency and low running resistance

Applications

For high speed reverse cleaning or low-pressure arm recovery filtration bag house, mainly used in cement and carbon black industry

Technical performance parameters

Weight（g/㎡）		550
Substrate		E-fiberglass Bulked Yarn Woven
Membrane		e-PTFE
Acid Resistance		Good
Alkali Resistance		Common
Tensile Strength （N/50mm）	Warp	≥3400
	Weft	≥2400
Air Permeability（cm/s@127Pa）		15～35(2~5)
Thickness（mm）		0.60±0.05
Continuous Operating Temp（℃）		<260
Max Momentary Operating Temp（℃）		280
Recommend Air Flow(m/min（m/min）		<0.60